High‐Performance, Room Temperature, Ultra‐Broadband Photodetectors Based on Air‐Stable PdSe₂

Abstract Photodetection over a broad spectral range is crucial for optoelectronic applications such as sensing, imaging, and communication. Herein, a high‐performance ultra‐broadband photodetector based on PdSe 2 with unique pentagonal atomic structure is reported. The photodetector responds from visible to mid‐infrared range (up to ≈4.05 µm), and operates stably in ambient and at room temperature. It promises improved applications compared to conventional mid‐infrared photodetectors. The highest responsivity and external quantum efficiency achieved are 708 A W −1 and 82 700%, respectively, at the wavelength of 1064 nm. Efficient optical absorption beyond 8 µm is observed, indicating that the photodetection range can extend to longer than 4.05 µm. Owing to the low crystalline symmetry of layered PdSe 2 , anisotropic properties of the photodetectors are observed. This emerging material shows potential for future infrared optoelectronics and novel devices in which anisotropic properties are desirable.